Superduplex roestvrij staalbieden een veel hogere sterkte en corrosiebestendigheid dan 316. Daarom is het onmiddellijke antwoord ja – superduplex is beter dan316.
'Duplex' stainless steels are a family of stainless steels that contain a mixed microstructure of austenite and ferrite phases. They offer a combination of good corrosion resistance and high strength, making them suitable for a wide range of applications. Super duplex stainless steels have a higher content of alloying elements, such as chromium, nickel, and molybdenum, compared to duplex stainless steels. They are based upon 25% chromium content. As such, super duplex stainless steels have up to four times the tensile strength of 316 stainless steel, and considerably better corrosion resistance. An alloys resistance to pitting corrosion can be usefully summarised by the PREN value, which is the 'Pitting Resistance Equivalent number'. The PREN for super duplex stainless steels is >40, vergeleken met de PREN voor 316 van 25.
Ondanks de zeer aantrekkelijke voordelen van superduplex roestvast staal boven 316 zijn er echter enkele beperkingen. Superduplex roestvast staal verliest veel van zijn slagvastheid onder -50degC, terwijl bij 316 de slagvastheid grotendeels behouden blijft tot aan cryogene temperaturen. Superduplex roestvast staal is beperkt tot bedrijfstemperaturen op lange termijn onder 250 graden Celsius, terwijl 316 tot 870 graden Celsius kan worden gebruikt (zolang het maar een koolstofarm staal is).316Lof titaniumgestabiliseerde 316Ti-varianten om intergranulaire corrosie te voorkomen).
Superduplex roestvast staal is zeker moeilijker te bewerken, gezien hun veel hogere sterkte. Ze worden gezien als moeilijker te lassen, maar kunnen gemakkelijk worden vervaardigd met de juiste apparatuur en procedures.